Page 177 - Riem-Vol6_nº2

348 IBRACON Structures and Materials Journal • 2013 • vol. 6 • nº 2
Is it possible to exceed the time limit specified by Brazilian Standard NBR 7212 for mixing and
transporting concrete?
exceed the time limits specified by Brazilian Standard NBR 7212,
as long as that the concrete workability is maintained by adding a
superplasticizer under constant agitation and no water is added until
concrete placement. Further studies with other concrete types and
mixing temperatures, among other variables, can be performed to
consolidate the procedures used in this test and contribute signifi-
cantly with decisions made in real life conditions regarding the possi-
bility of accepting or rejecting concrete shipments when mixing and
transportation periods do not comply with the standard.
5. Acknowledgements
The authors would like to thank NORIE (Research Group for In-
novation in Construction) of the Federal University of Rio Grande
do Sul (UFRGS) for their support with the tests and to the Concreto
Redimix do Brasil S/A company for their support and the opportu-
nity to perform studies in situ .
6. References
[01] ALHOZAIMY, A. M. Effect of retempering on the
compressive strength of ready-mixed concrete in
hot-dry environments. Cement & Concrete
Composites 29, 124-127, 2007.
[02] ASSOCIAÇÃO BRASILEIRA DE NORMAS TÉCNICAS
NBR 5738: Concreto - Procedimento para moldagem
e cura de corpos de prova. Rio de Janeiro: ABNT,
2003. 3p.
[03] ______ NBR 5739: Ensaios de compressão de
corpos-de-prova cilíndricos. São Paulo, 2007. 9p.
[04] ______ NBR 7212: Execução de concreto dosado
em central. Rio de Janeiro: ABNT, 1984. 7p.
[05] ______ NBR 11578: Cimento Portland composto.
Rio de Janeiro: ABNT, 1991. 5 p.
[06] ______ NBR NM 45: Agregados – Determinação
da massa unitária e do volume de vazios. Rio de
Janeiro: ABNT, 2006. 8p.
[07] ______ NBR NM 67: Concreto – Determinação da
consistência pelo abatimento do tronco de cone.
Rio de Janeiro: ABNT, 1998. 8p.
[08] ______ NBR NM 248: Agregados – determinação da
composição granulométrica. Rio de Janeiro: ABNT,
2003. 6p.
[09] COLLERPADI, M. Admixtures-enhancing concrete
performance. 6th International Congress, Global
Construction, Ultimate Concrete Opportunities,
Dundee, U.K. July 2005.
[10] DEWAR, J.D.; ANDERSON, R. Manual of ready
mixed concrete. Blackie Academic and Professional,
second ed., Glasgow, UK, 1992.
[11] ERDOĞDU, S. Effect of retempering with superplasticizer
admixtures on slump loss and compressive strength of
concrete subjected to prolonged mixing. Cement &
Concrete Research 35, 907-912, 2005.
[12] HEIKAL, M.; MORSY, M. S.; AIAD, I. Effect of
treatment temperature on the early hydration
characteristics of superplasticized silica fume blended
cement pastes. Cement & Concrete Research 35,
680-687, 2005.
[13] KIRCA, Ö.; TURANLI, L.; ERDOĞAN, T. Effects of
retempering on consistency and compressive strength
of concrete subjected to prolonged mixing. Cement &
Concrete Research 32, 441-445, 2002.
[14] MEHTA, P.K.; MONTEIRO, P.J.M. Concreto:
Microestrutura, Propriedades e Materiais. 3.ed.
São Paulo: IBRACON, 2008.
[15] POLESELLO, E. Avaliação da resistência à
compressão e da absorção de água de concretos
utilizados após o tempo máximo de mistura e
transporte especificado pela NBR 7212. (Dissertação
de Mestrado) Engenharia Civil, Universidade Federal
do Rio Grande do Sul, Porto Alegre, 2012.
[16] TEIXEIRA, R. B.; PELISSER, F. Análise da perda de
resistência à compressão do concreto com adição
de água para correção da perda de abatimento ao
longo do tempo. Revista de Iniciação Científica da
UNESC, Vol. 5, No 1, 2007.
[17] WEIDMANN, D. F.; OLIVEIRA, A. L.; SOUZA,
J.; PRUDÊNCIO JR, L. R.; BIACHINI, M. Avaliação
do desempenho de aditivos redutores de água para o
uso em centrais de concreto: estudo de caso,
49º Congresso Brasileiro do Concreto. Bento
Gonçalves-RS, IBRACON, 2007.